ʻO nā kristal AgGaS2


  • Nā ʻāpana lattice:a = 5.757, c = 10.311 Å
  • Lae hehee:997 °C
  • ʻAiʻa:4.702 g/cm3
  • Mohs paakiki:3-3.5
  • Ka helu hoʻopalekana:0.6 knm-1 @ 10.6 µm
  • Hoʻohui Dielectric mau @ 25:ε11s=10ε11t=14
  • Huahana Huahana

    Nā Kūlana ʻenehana

    Hoike Hoao

    Papa helu waiwai

    ʻIke ʻia ka AGS mai 0.50 a i 13.2 µm.ʻOiai ʻo ka helu helu ʻike ʻole ʻole ka haʻahaʻa loa ma waena o nā kristal infrared i ʻōlelo ʻia, hoʻohana ʻia ke aniani pōkole pōkole kiʻekiʻe ma 550 nm i nā OPO i puhi ʻia e Nd:YAG laser;i loko o nā ʻokoʻa like ʻole e hui pū ana i nā hoʻokolohua me ka diode, Ti: Sapphire, Nd:YAG a me IR dye lasers e uhi ana i ka laulā 3-12 µm;i nā ʻōnaehana countermeasure infrared, a no ka SHG o CO2 laser.Ua kaulana nā pā aniani ʻo AgGaS2 (AGS) no ka hoʻokumu ʻana i ka pulse ultrashort ma waena o ka laulā IR ma o ka ʻokoʻa ʻokoʻa o ka hoʻohana ʻana i nā pulse lōʻihi NIR.

    Nā noi:
    • Generation lua harmonics ma CO a me CO2 - lasers
    • Optical parametric oscilator
    • ʻOkoʻa alapine generator i waena infrared māhele a hiki i 12μm.
    • Ka hui 'ana ma ka waena IR mai 4.0 a 18.3 µm
    • Nā lasers moku'āina paʻa hiki ke hoʻokani ʻia (OPO i puhi ʻia e Nd:YAG a me nā lasers ʻē aʻe e hana ana ma ka ʻāpana 1200 a 10000 nm me ka maikaʻi 0.1 a 10 %)
    • Nā kānana ʻāiki ʻokiʻoki ma ka ʻāina kokoke i ka lae isotropic (0.4974 m ma 300 °K), hoʻokani ʻia ka pūna hoʻouna ma ke ʻano wela.
    • Ka hoʻololi ʻana o ke kiʻi hoʻoheheʻe laser CO2 i loko o kahi kokoke-IR a i ʻole ʻāpana ʻike ʻia ma o ka hoʻohana ʻana/a i ʻole ka hoʻohana ʻana i nā lasers Nd:YAG, ruby ​​a i ʻole dye me ka maikaʻi a hiki i 30 %
    Na Waiwai Kumu
    Nā ʻāpana lattice a = 5.757, c = 10.311 Å
    ʻAʻole laina laina ma 10.6 um d36 = 12.5 pm/V
    ʻO ka paepae pōʻino Optical ma 10.6 um, 150 ns 10 - 20 MW/cm2
    kaulike me ka axis c 12.5 x 10-6 x °C-1
    kū pololei i ka axis c -13.2 x 10-6 x °C-1
    Hoʻomoe Crystal Tetragonal
    Nā ʻāpana kelepona a=5.756 Å, c=10.301 Å
    Lae hehee 997 °C
    ʻO ka mānoanoa 4.702 g/cm3
    Mohs Paʻakikī 3-3.5
    Hoʻopili ʻana 0.6 knm-1 @ 10.6 µm
    Pilikia Dielectric mau @ 25 MHz ε11s=10ε11t=14
    ʻO ka hoʻonui wela wela ||C: -13.2 x 10-6 /oC⊥C: +12.5 x 10-6 /oC
    ʻO ka hoʻoili wela 1.5 W/M/°C

     

    Nā Kūlana ʻenehana
    ʻO ka ʻāweʻe nalu emi mai λ/6 @ 633 nm
    Ka hoʻomanawanui ana (W +/-0.1 mm) x (H +/-0.1 mm) x (L +0.2 mm/-0.1 mm)
    Mākaʻikaʻi puka > 90% wahi kikowaena
    Palahalaha λ/6 @ 633 nm no T>=1.0mm
    Ka maikaʻi o ka ʻili ʻEli/ʻeli 20/10 no MIL-O-13830A
    Hoʻolikelike ʻoi aku ka maikaʻi ma mua o 1 arc min
    Perpendicularity 5 mau minuke arc
    ʻO ka ʻae ʻana i ke kihi Δθ < +/-0.25o, Δφ < +/-0.25o

    测试图1图片2

    Hoʻohālike

    Huahana Nui Kūlana Ili mauna

    Ka nui

    DE0053

    AGS 5*5*0.5mm θ=41.3°;φ=0° AR/AR@1.1-2.6μm+2.6-12μm ʻAʻole kau ʻia

    1

    DE0093

    AGS 8*8*1mm θ=39°;φ=45° Ua poni ʻia nā ʻaoʻao ʻelua φ25.4mm

    3

    DE0119-0

    AGS 8*8*1mm θ=39°;φ=45° AR/AR@1.1-2.6μm+2.6-12μm φ25.4mm

    3

    DE0119-3

    AGS 8*8*1mm θ=39°;φ=45° AR/AR@1.1-2.6μm+2.6-12μm ʻAʻole kau ʻia

    2

    DE0119-1

    AGS 8*8*1mm θ=37°;φ=45° AR/AR@1.1-2.6μm+2.6-12μm ʻAʻole kau ʻia

    3

    DE0149

    AGS 8*8*0.38mm θ=41.6°;φ=45° AR/AR@1.1-2.6μm+2.6-12μm ʻAʻole kau ʻia

    1

    DE0367

    AGS 8*8*0.4mm θ=39°;φ=45° AR/AR@1.1-2.6μm+2.6-12μm φ25.4mm

    1

    DE0367-0

    AGS 8*8*0.4mm θ=39°;φ=45° AR/AR@1.1-2.6μm+2.6-12μm ʻAʻole kau ʻia

    1

    DE0367-1

    AGS 8*8*0.4mm θ=37°;φ=45° AR/AR@1.1-2.6μm+2.6-12μm ʻAʻole kau ʻia

    3

    DE0367-2

    AGS 8*8*0.4mm θ=37°;φ=45° AR/AR@1.1-2.6μm+2.6-12μm φ25.4mm

    1